If the newly discovered phenomenon can be harnessed, it could usher in an engineering revolution—one in which self-healing engines, bridges, and airplanes could reverse damage caused by wear and tear, making them safer and longer-lasting.

The research team from Sandia National Laboratories and Texas A&M University described their findings today in the journal Nature.

"This was absolutely stunning to watch first-hand," said Sandia materials scientist Brad Boyce.

"What we have confirmed is that metals have their own intrinsic, natural ability to heal themselves, at least in the case of fatigue damage at the nanoscale," he told the Laboratory's press.

Repeated stress or motion causes microscopic cracks to form in machines' metal components. Over time, these cracks grow and spread until the whole device breaks, or in the scientific lingo, it fails.

The fissure Boyce and his team saw disappear was one of these tiny but consequential fractures—measured in nanometers.

"From solder joints in our electronic devices to our vehicle's engines to the bridges that we drive over, these structures often fail unpredictably due to cyclic loading that leads to crack initiation and eventual fracture," Boyce said. "When they do fail, we have to contend with replacement costs, lost time and, in some cases, even injuries or loss of life. The economic impact of these failures is measured in hundreds of billions of dollars every year for the U.S."